Product finish |
Code |
Steel base |
Tinplate/ECCS |
Flow-melted |
Nominal surface roughness of the steel base um |
|
|
|
|
|
|
Bright |
BR |
Smooth |
TPL |
Yes |
<0,35 |
Fine stone |
FS |
Fine stone |
TPL |
Yes |
0,25-0,45 |
Fine stone |
FS |
Fine stone |
ECCS | - | 0,25-0,45 |
Stone | ST | Stone | TPL | Yes | 0,35-0,60 |
Stone | ST | Stone | ECCS | - | 0,35-0,60 |
Silver | SG | Shot blast | TPL | Yes | >0,90 |
Matt | MM | Shot blast | TPL | No | Various |
EUROPEAN STANDARD DRAFT prEN 10202 Tinplate Single spot values for tin coatings
Nominal coating |
High speed welding applications* |
Other applications | ||
(HS) | (SP) | |||
g/m2 | g/m2 | g/m2 | g/m2 | g/m2 |
min | max | min | max | |
1,00 | 0,75 | 1,80 | 0,75 | |
1,40 | 1,10 | 2,30 | 1,10 | |
2,00 | 1,60 | 3,00 | 1,60 | |
2,80 | 2,30 | 3,90 | 2,30 | |
4,00 | 3,35 | 5,30 | 3,35 | |
5,00 | 4,20 | 6,50 | 4,20 | No technical |
5,60 | 4,70 | 7,20 | 4,70 | requirement |
8,40 | 7,15 | 7,15 | ||
11,20 | 9,55 | 9,55 | ||
14,00 | 11,95 | No technical | 11,95 | |
15,10 | 12,90 | requirement | 12,90 | |
*Continuous electrical resistance welding at speeds greater than 30m/min |
EUROPEAN STANDARD DRAFT prEN 10202 Tinplate ECCS masses
Coating mass (mg/m2)each surface | ||
min | max | |
Total chromium | 50 | 140 |
Chromium in oxides | 7 | 35 |
NOTE Total chromium is the sum of the metallic chromium and chromium content of the oxides and hydroxides. |
EUROPEAN STANDARD DRAFT prEN 10202 Tinplate Mechanical properties of tinmill products
Yield/0,2%Proof strenght(Rp)- | Tensile strenght(Rm)- | |||||
N/mm2 | N/mm2 | |||||
New grades | Steel number | Nominal values | Dev. | Aim values | Dev. | |
TS230 | 1.0371 | 230 | _+ 50 | 325 | _+ 50 | |
TS245 | 1.0372 | 245 | _+ 50 | 340 | _+ 50 | |
TS260 | 1.0379 | 260 | _+ 50 | 360 | _+ 50 | |
TS275 | 1.0375 | 275 | _+ 50 | 375 | _+ 50 | |
TS290 | 1.0381 | 290 | _+ 50 | 390 | _+ 50 | |
TS550 | 1.0385 | 550 | _+ 50 | 575 | _+ 50 | |
TH415 | 1.0377 | 415 | _+ 50 | 435 | _+ 50 | |
TH435 | 1.0378 | 435 | _+ 50 | 460 | _+ 50 | |
TH520 | 1.0384 | 520 | _+ 50 | 540 | _+ 50 | |
TH550 | 1.0373 | 550 | _+ 50 | 570 | _+ 50 | |
TH580 | 1.0382 | 580 | _+ 50 | 590 | _+ 50 | |
TH620 | 1.0374 | 620 | _+ 50 | 625 | _+ 50 | |
|
EUROPEAN STANDARD DRAFT prEN 10202 Tinplate
Purchasers should agree with their suppliers the type to be ordered for specific applications, noting that type B is not suitable for welding. Chemical composition of continuously cast steels. |
Element | %by weight (maximun unless otherwise stated) | |
Type A | Type B | |
Carbon | 0,048-0,08 | 0,09-0,12 |
Manganese | 0,18-0,35 | 0,30-0,50 |
Sulphur | 0,020 | 0,020 |
Phosphorus | 0,020 | 0,020 |
Silicon | 0,030 | 0,030 |
Copper | 0,080 | 0,080 |
Nickel | 0,080 | 0,080 |
Tin | 0,020 | 0,020 |
Arsenic | 0,020 | 0,020 |
Molybdenum | 0,020 | 0,020 |
Chromium | 0,080 | 0,080 |
Nitrogen | 0,008 | 0,008 |
Aluminium | 0,02-0,08 | 0,02-0,08 |
Others | 0,020 | 0,020 |
Note 1 Individual chemical elements can by agreement be modified to suit special applications. | ||
Note 2 Chemical elements included as Others are those which occur naturally in very small quantities but which are not deliberately added in the steel making process. |
|
|